Název: | Mechanical properties and temperature stability of modified polybutylene terephthalate by beta rays | ||||||||||
Autor: | Mizera, Aleš; Maňas, Miroslav; Maňas, David; Stoklásek, Pavel; Bednařík, Martin; Hýlová, Lenka | ||||||||||
Typ dokumentu: | Článek ve sborníku (English) | ||||||||||
Zdrojový dok.: | MATEC Web of Conferences 20th International Conference on Circuits, Systems, Communications and Computers (CSCC 2016). 2016, vol. 76 | ||||||||||
ISSN: | 2261-236X (Sherpa/RoMEO, JCR) | ||||||||||
Journal Impact
This chart shows the development of journal-level impact metrics in time
|
|||||||||||
DOI: | https://doi.org/10.1051/matecconf/20167602031 | ||||||||||
Abstrakt: | The presented article deals with the research of mechanical properties before and after temperature load and temperature stability of modified polybutylene terephthalate by radiation cross-linking. The mechanical properties were measured, at the ambient temperature, by the tensile test on samples which were non-irradiated and irradiated by different doses of the beta radiation and then were temperature loaded. Results demonstrate that PBT has higher values of tensile strength with the increased irradiation dose and it has decreased elongation at break sharply. The purpose of the article is to consider to what extent the irradiation process influences the resulting mechanical properties and temperature stability. The PBT tested showed significant improvement of temperature stability after irradiation. This behaviour leads to the expansion of these materials in the automotive and electrical industry. | ||||||||||