Název: | Biodegradability and Mechanical Properties of Poly(vinyl alcohol)-Based Blend Plastics Prepared Through Extrusion Method | ||||||||||
Autor: | Kopčilová, Martina; Hubáčková, Jitka; Růžička, Jan; Dvořáčková, Marie; Julinová, Markéta; Koutný, Marek; Tomalová, Miroslava; Alexy, Pavol; Bugaj, Peter; Filip, Jaroslav | ||||||||||
Typ dokumentu: | Recenzovaný odborný článek (English) | ||||||||||
Zdrojový dok.: | Journal of Polymers and the Environment. 2013, vol. 21, issue 1, p. 88-94 | ||||||||||
ISSN: | 1566-2543 (Sherpa/RoMEO, JCR) | ||||||||||
Journal Impact
This chart shows the development of journal-level impact metrics in time
|
|||||||||||
DOI: | https://doi.org/10.1007/s10924-012-0520-8 | ||||||||||
Abstrakt: | Plastic blend materials consisting of poly(vinyl alcohol), glycerol and xanthan or gellan were prepared through laboratory extrusion. Their base mechanical properties were compared with the properties of poly(vinyl alcohol) foil and their biodegradability in soil, compost and both activated and anaerobic sludge were assessed. In samples with lower polysaccharide content (10-21 %w/w) the tensile strength of 15-20 MPa was found; the elongation at break of all blends was relatively close to the parameter of poly(vinyl alcohol) foil. The biodegradability levels of the blends tested corresponded to the content of natural components, and the mineralization of the samples with the highest carbohydrate proportion (42 %) reached 50-78 %, depending on the type of the environment. Complete biodegradation of all samples occurred in activated sludge. © 2012 Springer Science+Business Media, LLC. | ||||||||||